Rosemary oil as a corrosion inhibitor for carbon steel in 0.5 M sulfuric acid solution
Rosemary oil as a corrosion inhibitor for carbon steel in 0.5 M sulfuric acid solution
 
الموضوع : كيمياء 
لغة الوثيقة : الانجليزية 
المستخلص : The possibility of using rosemary oil as a corrosion inhibitor of carbon steel in 0.5 M sulfuric acid solution was investigated by determination of weight loss, potentiodynamic polarization, and electrochemical impedance spectroscopy. It was shown that the inhibition effectiveness increases with an increase in the concentration of oil and a decrease in the temperature. The inhibiting effect of the investigated oil is due to its adsorption on the surface of the steel and complexation. Adsorption is described by a Langmuir isotherm. The effect of the temperature on the corrosion rate was studied in the presence and absence of the oil and the thermodynamic parameters of the corrosion process were calculated. 
ردمد : 0009-3092 
اسم الدورية : Chemistry and Technology of Fuels and Oils 
المجلد : 47 
العدد : 1 
سنة النشر : 1432 هـ
2011 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Saturday, February 11, 2012 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
فوزية محمد النويصرAl-Nowaiser, Fawziya Mباحثدكتوراهfalnowaiser@kau.edu.sa
متولي عبداللهAbdallah, M باحثدكتوراه 
السيد حسيني المسلميEl-Mossalamy, El-sayed Hباحثدكتوراهsbdmina@yahoo.com

الملفات

اسم الملفالنوعالوصف
 32234.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث